| Grade : | X10CrNi18-8 | ||||||
| Number: | 1.4310 | ||||||
| Classification: | Austenitic stainless steel | ||||||
| Density: | 7.9 g/cm ³ | ||||||
| Standard: |
| ||||||
| Equivalent grades: | Go here |
| Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. |
| C | Si | Mn | Ni | P | S | Cr | Mo | N |
| 0.05 - 0.15 | max 2 | max 2 | 6 - 9.5 | max 0.045 | max 0.015 | 16 - 19 | max 0.8 | max 0.11 |
| Rm - Tensile strength (MPa) (+A) | 500-750 |
| Rm - Tensile strength (MPa) (+AT+C) | 850-890 |
| Rp0.2 0.2% proof strength (MPa) (+A) | 195-250 |
| A - Min. elongation at fracture (%) (+A) | 40 |
| Nominal diameter (mm): | 2 - 25 |
| Z - Reduction in cross section on fracture (%) | 60-65 |
| Brinell hardness (HB): (+A) | 230 |
| Resistance to intergranular corrosion: in the delivery condition - no; in the sensitized condition - no |
| EU EN | USA - | Germany DIN,WNr | Japan JIS | France AFNOR | England BS | Sweden SS | Inter ISO | |||||||||
| X10CrNi18-8 |
|
|
|
|
|
|
|
| ReH | Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Tensile strength / Zugfestigkeit / Resistance a la traction |
| A | Minimum elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Notch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
|
Chemical composition of steel X10CrNi18-8 (1.4310), Standards of steel X10CrNi18-8 (1.4310) Mechanical Properties of steel X10CrNi18-8 (1.4310) Equivalent grades of steel X10CrNi18-8 (1.4310) steel X10CrNi18-8 (1.4310) Tensile Strength, Elongation, Proof strength , Hardness |