EN-GJS-450-10   ( 5.3107 )

    Grade :     EN-GJS-450-10
    Number:     5.3107
    Classification:     Spheroidal graphite cast iron
    Density:     7.1   g/cm ³
    Standard:
    EN 1563: 2011 Founding. Spheroidal graphite cast irons
    Equivalent grades:     Go here



Chemical composition %   of grade   EN-GJS-450-10 (5.3107):   EN 1563-2005
-
The chemical composition shall be left to the discretion of the manufacturer


Mechanical properties of grade   EN-GJS-450-10 (5.3107)

Nominal thickness (mm):   to 30
Rm - Tensile strength (MPa)450


Nominal thickness(mm):   to 30
Rp0.2 0.2% proof strength (MPa)310


Nominal thickness (mm):     to 30
A - Min. elongation at fracture (%) 10


  Brinell hardness   (HBW):   160 - 210


Equivalent grades of grade   EN-GJS-450-10 (5.3107)
Warning! Only for reference

USA
-
Japan
JIS
France
AFNOR
England
BS
European old
EN
Italy
UNI
Belgium
NBN
Spain
UNE
China
GB
Bulgaria
BDS
Hungary
MSZ
Poland
PN
Austria
ONORM
Australia
AS
Russia
GOST
Inter
ISO
India
IS
Netherlands
NEN
Luxembourg
-
COPANT
-
65-45-12
70-50-05
FCD450
FCD450-10
450-10
FGS450-10
420/12
450/10
EN-JS1040
GS400-12
FNG42-12
FGE42-12
QT450-10
400-12
GoV40
ZS4012
SG42
400-12
VCH45
450-10
450-10/S
450-10/U
SG400/12
GN42
FNG42-12
FMNP45007


Mechanical properties
ReH Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale
Rm Tensile strength / Zugfestigkeit / Resistance a la traction
A Minimum elongation / Mindestwert der Bruchdehnung / Allongement minimal
J Notch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc

Spheroidal graphite cast iron   EN-GJS-450-10 (5.3107)
Chemical composition , Equivalent grades , Standards, Properties , Hardness , Strength , Elongation