EN-GJS-400-15   ( 5.3106 )


    Grade :     EN-GJS-400-15
    Number:     5.3106
    Classification:     Spheroidal graphite cast iron
    Standard:
    EN 1563: 2011 Founding. Spheroidal graphite cast irons
    Equivalent grades:     Go here



Chemical composition %   of grade   EN-GJS-400-15 (5.3106):   EN 1563-2005
-
The chemical composition shall be left to the discretion of the manufacturer


Mechanical properties of grade   EN-GJS-400-15 (5.3106)

Nominal thickness (mm):   to 3030 - 6060 - 200
Rm - Tensile strength (MPa)400390370


Nominal thickness(mm):   to 3030 - 6060 - 200
Rp0.2 0.2% proof strength (MPa)250250240


Nominal thickness (mm):     to 3030 - 6060 - 200
A - Min. elongation at fracture (%) 151411


  Brinell hardness   (HBW):   135 - 180


Equivalent grades of grade   EN-GJS-400-15 (5.3106)
Warning! Only for reference
USA
-
Germany
DIN,WNr
Japan
JIS
France
AFNOR
England
BS
European old
EN
Italy
UNI
China
GB
Sweden
SS
Norway
NS
Russia
GOST
Inter
ISO
Netherlands
NEN
60-40-18
65-45-12
0.7040
GGG40
FCD400
FCD400-15
400-15
FGS-400-12
FGS400-15
420/12
EN-JS1030
GS400-12
QT400-15
0717-02
17-00
SJK-400
VCH40
400-15
400-15/S
400-15/U
GN42


Mechanical properties
ReH Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale
Rm Tensile strength / Zugfestigkeit / Resistance a la traction
A Minimum elongation / Mindestwert der Bruchdehnung / Allongement minimal
J Notch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc

  EN-GJS-400-15 (5.3106) - Spheroidal graphite cast iron
Chemical composition , Equivalent grades of Cast iron, Standards, Mechanical Properties, Hardness , Strength , Elongation